Bis-GMA复合牙科材料的合成和抗菌改性

朱琳琳, 杨俊, 郑安呐, 危大福, 管涌

(华东理工大学材料科学与工程学院，上海市先进聚合物材料重点实验室，超细材料制备与应用教育部重点实验室，上海 200237)

Synthesis and Antibacterial Activity of Bis-GMA Dentine Primer

ZHU Lin-lin, YANG Jun, ZHENG An-na, WEI Da-fu, GUAN Yong

(Shanghai Key Laboratory of Advanced Polymeric Materials, Key Laboratory for Ultrafine Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237，China)

摘要

图/表

参考文献

相似文献

本文已被：浏览 1663次下载 1623次
投稿时间：2011-12-08

中文摘要: 以甲基丙烯酸缩水甘油酯（GMA）修饰聚六亚甲基胍盐酸盐（PHMG），制备端基具有甲基丙烯酸酯基的抗菌改性剂PHMG-GMA。将PHMG-GMA与树脂双酚A-甲基丙烯酸缩水甘油酯（Bis-GMA）、稀释剂二甲基丙烯酸二缩三乙二醇酯（TEGDMA）、填料纳米SiO2、光引发剂樟脑醌（CQ）混合均匀，经紫外灯固化后得到了具有抗菌性能的复合牙科材料。测试了该材料的抗菌性能，研究了SiO2、PHMG-GMA的加入对紫外透过率的影响。结果表明：随着SiO2含量的增加，材料的紫外透过率下降。当PHMG-GMA的质量分数

中文关键词: Polyhexamethylene guanidine (PHMG) with reactive methacrylate group, named as PHMG-GMA, was prepared by the reaction between polyhexamethylene guanidine (PHMG) and glycidyl methacrylate (GMA). After homogeneously blending of nano-SiO2, PHMG-GMA, bisphenol

Abstract:聚六亚甲基胍盐酸盐；双酚A-甲基丙烯酸缩水甘油酯；复合牙科材料；抗菌率

keywords: PHMG Bis-GMA dental composite antibacterial rate

文章编号： 中图分类号： 文献标志码：

基金项目:国家自然科学基金项目（50573020）；教育部留学归国人员科研启动基金资助项目

作者	单位	E-mail
朱琳琳	华东理工大学材料科学与工程学院，上海市先进聚合物材料重点实验室，超细材料制备与应用教育部重点实验室，上海 200237	linlin198708@yahoo.cn
杨俊	华东理工大学材料科学与工程学院，上海市先进聚合物材料重点实验室，超细材料制备与应用教育部重点实验室，上海 200237
郑安呐	华东理工大学材料科学与工程学院，上海市先进聚合物材料重点实验室，超细材料制备与应用教育部重点实验室，上海 200237	zan@ecust.edu.cn
危大福	华东理工大学材料科学与工程学院，上海市先进聚合物材料重点实验室，超细材料制备与应用教育部重点实验室，上海 200237
管涌	华东理工大学材料科学与工程学院，上海市先进聚合物材料重点实验室，超细材料制备与应用教育部重点实验室，上海 200237

Author Name	Affiliation	E-mail
ZHU Lin-lin	Shanghai Key Laboratory of Advanced Polymeric Materials, Key Laboratory for Ultrafine Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237，China	linlin198708@yahoo.cn
YANG Jun	Shanghai Key Laboratory of Advanced Polymeric Materials, Key Laboratory for Ultrafine Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237，China
ZHENG An-na	Shanghai Key Laboratory of Advanced Polymeric Materials, Key Laboratory for Ultrafine Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237，China	zan@ecust.edu.cn
WEI Da-fu	Shanghai Key Laboratory of Advanced Polymeric Materials, Key Laboratory for Ultrafine Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237，China
GUAN Yong	Shanghai Key Laboratory of Advanced Polymeric Materials, Key Laboratory for Ultrafine Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237，China

引用本文：
朱琳琳,杨俊,郑安呐,危大福,管涌.Bis-GMA复合牙科材料的合成和抗菌改性[J].功能高分子学报,2012,25(3):.
ZHU Lin-lin,YANG Jun,ZHENG An-na,WEI Da-fu,GUAN Yong.Synthesis and Antibacterial Activity of Bis-GMA Dentine Primer[J].Journal of Functional Polymers,2012,25(3):.

用微信扫一扫