中文摘要: 采用接枝共聚法合成了以聚乙二醇（PEG）为相变物质，沸石为骨架的PEG 沸石固 固相变材料。通过红外光谱（FT-IR）、热失重分析（TGA）和差示扫描量热法（DSC）等测试手段对PEG-沸石固-固相变材料的结构、相变行为及热稳定性进行了研究。结果表明：通过改变PEG的分子量，可以得到不同相变焓和不同相变温度的PEG 沸石固-固相变材料，其相变焓可达105.41 J/g，热稳定性良好，起始分解温度高于300 ℃。
Abstract:PEG-zeolite solid-solid phase change material was synthesized by graft copolymerization. Polyethylene glycol(PEG) was used for phase change material and zeolite for skeleton. Infrared spectrometry (FT-IR), thermogravimetry analysis(TGA) and differentia scanning calorimetric(DSC) were used to study the microstructure, phase change behavior and thermal stability of PEG-zeolite solid-solid phase change material. Results show that PEG-zeolite solid-solid phase change material has different phase transition enthalpy and phase transition temperature by changing the molecular weight of PEG. The phase change enthalpy is up to 105.41 J/g. The thermostability is so good that the initial decomposition temperature is higher than 300 °C.
文章编号： 中图分类号： 文献标志码：
基金项目:教育部科学技术研究重点项目(209040)
| 作者 | 单位 | |
| 顾晓华 | 齐齐哈尔大学材料学院， 黑龙江 齐齐哈尔 161006 | gxh219@yahoo.cn |
| 李世伟 | 齐齐哈尔大学材料学院， 黑龙江 齐齐哈尔 161007 | |
| 郑兵 | 江苏三房巷集团有限公司， 江苏 无锡 214423 | |
| 刘剑虹 | 齐齐哈尔大学材料学院， 黑龙江 齐齐哈尔 161006 |
引用本文：
顾晓华,李世伟,郑兵,刘剑虹.PEG-沸石固-固相变材料的制备及性能[J].功能高分子学报,2012,25(2):.
GU Xiao hua,LI Shi wei,ZHENG Bing,LIU Jian hong.Preparation and Properties of PEG-Zeolite Solid-Solid Phase Change Material[J].Journal of Functional Polymers,2012,25(2):.
顾晓华,李世伟,郑兵,刘剑虹.PEG-沸石固-固相变材料的制备及性能[J].功能高分子学报,2012,25(2):.
GU Xiao hua,LI Shi wei,ZHENG Bing,LIU Jian hong.Preparation and Properties of PEG-Zeolite Solid-Solid Phase Change Material[J].Journal of Functional Polymers,2012,25(2):.